The development of functionalized electrospun nanofibers for the control of pathogenic microorganisms in water.
- Authors: Kleyi, Phumelele Eldridge
- Date: 2014
- Subjects: Electrospinning , Nanofibers , Pathogenic microorganisms , Pathogenic microorganisms -- Detection , Drinking water -- Microbiology , Water quality -- Measurement , Imidazoles , Spectrum analysis , Anti-infective agents , Polymerization
- Language: English
- Type: Thesis , Doctoral , PhD
- Identifier: vital:4497 , http://hdl.handle.net/10962/d1013134
- Description: The thesis presents the development of functionalized electrospun nylon 6 nanofibers for the eradication of pathogenic microorganisms in drinking water. Imidazole derivatives were synthesized as the antimicrobial agents and were characterized by means of NMR spectroscopy, IR spectroscopy, elemental analysis and X-ray crystallography. The first set of compounds (2-substituted N-alkylimidazoles) consisted of imidazole derivatives substituted with different alkyl groups (methyl, ethyl, propyl, butyl, heptyl, octyl, decyl and benzyl) at the 1-position and various functional groups [carboxaldehyde (CHO), alcohol (CH2OH) and carboxylic acid (COOH)] at the 2-position. It was observed that the antimicrobial activity of the compounds increased with increasing alkyl chain length and decreasing pKa of the 2-substituent. It was also observed that the antimicrobial activity was predominantly against a Gram-positive bacterial strains [Staphylococcus aureus (MIC = 5-160 μg/mL) and Bacillus subtilis subsp. spizizenii (MIC = 5-20 μg/mL)], with the latter being the more susceptible. However, the compounds displayed poor antimicrobial activity against Gram-negative bacterial strain, E. coli (MIC = 150- >2500 μg/mL) and did not show any activity against the yeast, C. albicans. The second set of compounds consisted of the silver(I) complexes containing 2-hydroxymethyl-N-alkylimidazoles. The complexes displayed a broad spectrum antimicrobial activity towards the microorganisms that were tested and their activity [E. coli (MIC = 5-40 μg/mL), S. aureus (MIC = 20-80 μg/mL), Bacillus subtilis subsp. spizizenii (MIC = 5-40 μg/mL) and C. albicans (MIC = 40-80 μg/mL)] increased with the alkyl chain length of the 2-hydroxymethyl-N-alkylimidazole. The third set of compounds consisted of the vinylimidazoles containing the vinyl group either at the 1-position or at the 4- or 5- position. The imidazoles with the vinyl group at the 4- or 5-position contained the alkyl group (decyl) at the 1-position. For the fabrication of the antimicrobial nanofibers, the first two sets of imidazole derivatives (2-substituted N-alkylimidazoles and silver(I) complexes) were incorporated into electrospun nylon 6 nanofibers while the third set (2-substituted vinylimidazoles) was immobilized onto electrospun nylon 6 nanofibers employing the graft polymerization method. The antimicrobial nylon nanofibers were characterized by IR spectroscopy and SEM-EDAX (EDS). The electrospun nylon 6 nanofibers incorporated with 2-substituted N-alkylimidazoles displayed moderate to excellent levels of growth reduction against S. aureus (73.2-99.8 percent). For the electrospun nylon 6 nanofibers incorporated with silver(I) complexes, the levels of growth reduction were >99.99 percent, after the antimicrobial activity evaluation using the shake flask method. Furthermore, the grafted electrospun nylon 6 nanofibers showed excellent levels of growth reduction for E. coli (99.94-99.99 percent) and S. aureus (99.93-99.99 percent). The reusability results indicated that the grafted electrospun nylon 6 nanofibers maintained the antibacterial activity until the third cycle of useage. The cytotoxicity studies showed that grafted electrospun nylon 6 nanofibers possess lower cytotoxic effects on Chang liver cells with IC50 values in the range 23.48-26.81 μg/mL. The thesis demonstrated that the development of antimicrobial electrospun nanofibers, with potential for the eradication of pathogenic microoganisms in water, could be accomplished by incorporation as well as immobilization strategies.
- Full Text:
- Date Issued: 2014
Solvent-free synthesis of bisferrocenylimines and their coordination to rhodium (I)
- Authors: Kleyi, Phumelele Eldridge
- Date: 2009
- Subjects: Organic compounds -- Synthesis , Organic solvents , Solution (Chemistry) , Chemistry, Organic , Coordination compounds
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:10393 , http://hdl.handle.net/10948/1053 , Organic compounds -- Synthesis , Organic solvents , Solution (Chemistry) , Chemistry, Organic , Coordination compounds
- Description: Solvent-free reactions possess advantages compared to the solvent route, such as shorter reaction times, less use of energy, better yields, etc. Herein, the synthesis and characterization of bisferrocenylimines and arylbisamines are described. Reduction of the above compounds with LAH resulted in the formation of bisferrocenylamines and arylbisamines, respectively. The coordination chemistry of all the above compounds to rhodium(I) is also discussed in the prepared complexes [Rh(COD)(NN)]ClO4, where NN = bisferrocenylimines, and [Rh(COD)(NN)]BF4, where NN = bisferrocenylamines and arylbisamines. X-ray crystal structures of the complexes [Rh(COD)(NN)]ClO4 ([3.2] and [3.3]) have been obtained. Complexes of the type [Rh(COD)(NN)]BF4 were characterized with IR and UV-vis spectroscopy, cyclic voltammetry and conductometry. The catalytic activity of the complexes was also investigated: [Rh(COD)(NN)]ClO4 for the polymerization of phenylacetylene and [Rh(COD)(NN)]BF4 for the hydroformylation of styrene.
- Full Text:
- Date Issued: 2009